Let’s say I’m doing a fillet weld both pieces are 6mm thick. When I weld and check the backs and underneath of the plates there is no noticeable heat/penetration. Is this normal when you do thicker material and does that mean the joint has little if not any penetration and is weak?
I don’t see any difference when I turn the amps up. I would have thought running on my max amount of amps (260) I would see penetration through 6mm plate.
3-4mm plate is well penetrated just having problems noticing anything on anything higher than 5mm.
I don’t see any difference when I turn the amps up. I would have thought running on my max amount of amps (260) I would see penetration through 6mm plate.
3-4mm plate is well penetrated just having problems noticing anything on anything higher than 5mm.