Yep. I see where they're coming from. Point is, the weldpool is there, just covered (and protected) by a layer of oxide. If you poke the rod (best to use thicker rods than you normally would) through that layer, away you go. If you try and drip the rod at the weldpool, you get no adhesion worth mentioning, you have to poke!